METHODS ANALYSIS FOR PHASE MEASUREMENT IN WELDED SAMPLE OF SUPERDUPLEX STAINLESS STEEL UNS S32750

ANÁLISE DE MÉTODOS PARA CONTAGEM DE FASES EM AMOSTRAS SOLDADAS DO AÇO INOXIDÁVEL UNS S32750

Santos Júnior, Francisco Magalhães dos; Silvaa, Leonardo Oliveira Passos da; Seixas, Luã Fonseca; Lima, Tiago Nunes; Dourado, Alexandre Ferraz; Silva, Bruno Caetano dos Santos; Souza, Daniel Marques de; Coelho, Rodrigo Santiago

Artigo completo:

This study presents an evaluation of two methods to measure phases in welded samples of super duplex stainless steel UNS S32750. The aim is to identify the most suitable method for characterizing the microstructure of welded joints of this steel. In the color contrast method, it was found that there was no great variation in the results due to the low value of the standard deviation. While for the ASTM E 652 standard point counting method, the percentage values of ferrite found were slightly higher than the previous method. However, these two methods produced low standard deviations and, since the method described by the standard is possible to differentiate deleterious phases, this technique is the most suitable for the microstructure characterization for welded samples of super duplex stainless steel.

: Neste estudo é apresentada uma avaliação de dois métodos para contagem de fases em amostras soldadas do aço inoxidável super duplex UNS S32750. O objetivo é identificar o método mais adequado para caracterização da microestrutura de juntas soldadas desse aço. No método de contraste de cores, constatou-se que não houve grande variação dos resultados encontrados devido ao baixo valor do desvio padrão. Enquanto que para o método de contagem de pontos da norma ASTM E 652, os valores percentuais de ferrita encontrados foram ligeiramente superiores ao método anterior. No entanto, esses dois métodos produziram baixos desvios padrões e, uma vez que o método descrito pela norma é possível diferenciar fases deletérias, esta técnica é a mais adequada para a caracterização da microestrutura de aço inoxidável super duplex soldados e simulados termicamente.

Palavras-chave:

DOI: 10.5151/siintec2020-METHODSANALYSIS

Referências bibliográficas

• [1] 1 Z. Zhang, H. Zhao, H. Zhang, J. Hu, and J. Jin, “Microstructure evolution and pitting corrosion behavior of UNS S32750 super duplex stainless steel welds after short-time heat treatment,” Eval. Program Plann., vol. 121, pp. 22–31, 2017, doi: 10.1016/j.corsci.2017.02.006.
• [2] 2 G. Chail and P. Kangas, “Super and hyper duplex stainless steels: Structures, properties and applications,” Procedia Struct. Integr., vol. 2, pp. 1755–1762, 2016, doi: 10.1016/j.prostr.2016.06.221.
• [3] 3 L. O. P. da Silva, A. C. Nascimento, F. M. dos Santos Júnior, T. N. Lima, B. C. dos S. Silva, and R. S. Coelho, “Simulação Numérica E Física Na Soldagem Dos Aços Inoxidáveis Duplex: Uma Revisão Sistemática.,” pp. 373–380, 2019, doi: 10.5151/siintec2019-47.
• [4] 4 M. Schütze, Corrosion Books: Handbook of Corrosion Engineering. By Pierre R. Roberge - Materials and Corrosion 4/2002, vol. 53, no. 4. 2002.
• [5] 5 R. O. Dos Santos, M. R. S. Almeida, L. L. N. Guarieiro, and R. S. Coelho, “Analysis of the GTAW process influence on UNS S32760 superduplex steel microstructure and corrosion resistance,” Rev. Virtual Quim., vol. 8, no. 4, pp. 1040–1053, 2016, doi: 10.21577/1984-6835.20160074.
• [6] 6 F. Ribeiro, “Aplicação De Diferentes Técnicas De Microscopia Para A Quantificação De Fases Deleté Rias Presentes No Aço Inoxidável Superduplex Uns S32750,” Fortaleza, 2017.
• [7] 7 M. Breda, J. Basoni, F. Toldo, C. Bastianello, S. A. Ontiveros Vidal, and I. Calliari, “Comparative analysis on phase quantification methods in duplex stainless steels weldments,” Metall. Ital., vol. 107, no. 4, pp. 3–7, 2015.
• [8] 8 G. C. de Souza et al., “Avaliação da Proporção de Fases em Juntas Soldadas de Tubulações de Aço Inoxidável Duplex Mediante Aplicação de Ensaios Não Destrutivos,” Soldag. e Insp., vol. 18, no. 2, pp. 158–168, 2013, doi: 10.1590/S0104-92242013000200009.
• [9] 9 C. G. Camerini et al., “Avaliação Do Ferritoscópio Para Quantificação De Ferrita Delta Em Aços Inoxidáveis Superduplex,” vol. 72, pp. 2491–2501, 2017, doi: 10.5151/1516-392x-30710.
• [10] 10 A. Forgas Júnior, J. Otubo, and R. Magnabosco, “Ferrite quantification methodologies for duplex stainless steel,” J. Aerosp. Technol. Manag., vol. 8, no. 3, pp. 357–362, 2016, doi: 10.5028/jatm.v8i3.653.
• [11] 11 Astm, “Standard Test Method for Determining Volume Fraction by Systematic Manual Point Count E 562,” Practice, no. C, pp. 1–7, 2011, doi: 10.1520/E0562-11.2.
• [12] 12 A. Normas, “N-133 Soldagem,” 2017.
• [13] 13 I. N. Bastos and R. P. Nogueira, “Electrochemical noise characterization of heat-treated superduplex stainless steel,” Mater. Chem. Phys., vol. 112, no. 2, pp. 645–650, 2008, doi: 10.1016/j.matchemphys.2008.06.034.
• [14] 14 D. Arun, K. D. Ramkumar, and R. Vimala, “Multi-pass arc welding techniques of 12 mm thick super-duplex stainless steel,” J. Mater. Process. Tech., vol. 271, no. March, pp. 126–143, 2019, doi: 10.1016/j.jmatprotec.2019.03.031.
• [15] 15 Petrobras, “Technical Specification I-ET-3010.90-1200-955-PPC-002,” 2000.
• [16] 16 Z. Zhang, Z. Wang, Y. Jiang, H. Tan, D. Han, and Y. Guo, “Effect of post-weld heat treatment on microstructure evolution and pitting corrosion behavior of UNS S31803 duplex stainless steel welds,” Corros. Sci., vol. 62, pp. 42–50, 2012, doi: 10.1016/j.corsci.2012.04.047.

Como citar:

Santos Júnior, Francisco Magalhães dos ; Silvaa, Leonardo Oliveira Passos da ; Seixas, Luã Fonseca ; Lima, Tiago Nunes ; Dourado, Alexandre Ferraz ; Silva, Bruno Caetano dos Santos ; Souza, Daniel Marques de ; Coelho, Rodrigo Santiago ; "METHODS ANALYSIS FOR PHASE MEASUREMENT IN WELDED SAMPLE OF SUPERDUPLEX STAINLESS STEEL UNS S32750", p-163-171. In: Anais do VI Simpósio Internacional de Inovação e Tecnologia. São Paulo: Blucher, 2020.
ISSN 23577592, DOI 10.5151/siintec2020-METHODSANALYSIS