Analysis of intergranular corrosion in welded joints with ferritic stainless steel ISI 409 and AISI 439 for application in vehicular exhaustion systems

Amorim, Rafael Alves de; Lebrão, Susana Marraccini Giampietri; Colosio, Marco A.; Lara, José Agustín Castillo;

Artigo:

The goal of this work consist of evaluating the sensibility of intergranular corrosion in welded joints of AISI 409 e AISI 439 applied in vehicular exhaustion systems, considering the type of welding process as being manual and automatic. For acquiring the test results were performed in DL-EPR (Reactivation of Duplo Loop Dynamic Potential) with 0,5M of H2SO4 in 25°C, and mass lost according to ASTM A763 (Procedure X) for corrosion intergranular and ASTM G 48 (Method A) for pit corrosion. The results showed that corrosion depends on alloy elements in those steels and the increase of temperature in base metal due to weld wire speed.

Artigo:

Palavras-chave: ,

Palavras-chave: ,

DOI: 10.5151/simea2018-PAP76

Referências bibliográficas
  • [1] AGARELLI, G. ; LIMA, W. M. ; LEBRÃO, S. M. G. ; LARA, J. A. C. ; COLOSIO, M. A. . Análise da sensitização de juntas soldadas em aços inoxidáveis AISI 409 e AISI 439 para uso em sistema de exaustão veicular. In: 72o Congresso Internacional da ABM, 2017, São Paulo, 2017. ASTM A763 – Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels. 2015. ASTM G1 – Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens. 201 ASTM G48 – Standard Test Methods for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys by Use of Ferric Chloride Solution. 2015. Cobb, Harold M. The History of Stainless Steel – ASM Handbook, ASM International, 2010. Ferreira, Demostenes F., Soldabilidade do Aço Inoxidável Ferrítico. UFU (Universidade Federal de Uberlândia), Symposium of after graduation in mechanical engineering. 2006. Lebrão, S.M.G. Investigação sobre a resistência à corrosão intergranular do aço inoxidável austenítico UNS S31254. Thesi of doutorado, EPUSP, São Paulo, 1998. Lima, Luciana I. L.. Metodologia para avaliação da corrosão da zona termicamente afetada de aço inoxidável ferrítico AISI 439 soldado. UFMG (Universidade Federal de Minas Gerais), Program of de after graduation in mechanical engineering, 2007. Mei, P. R.; Silva, A. L. C. Aços e ligas especiais. 2 ed. Sumaré, SP: Eletrometal S. A. Metais Especiais, 1988. Modenesi, P. J., Apostila Soldabilidade dos Aços Inoxidáeis, Volum 1, SENAI, 2001 Serna-Giraldo, C. A. Resistencia à Corrosão Intergranular UNS S43000: avaliação por método de reativação eletroquímica, efeito de tratamento isotérmico e mecanismo de sensitização. Thesi of Doutorado. Escola Politécnica da Universidade of São Paulo. 2006 SERNA-GIRALDO, Carlos Augusto et al. Investigação do efeito do teor de intersticiais sobre o grau de sensitização em aços inoxidáveis ferríticos a 600ºC. Rev. Esc. Minas. 2007, vol.60, n.1, pp.49-54.
Como citar:

Amorim, Rafael Alves de; Lebrão, Susana Marraccini Giampietri; Colosio, Marco A.; Lara, José Agustín Castillo; "Analysis of intergranular corrosion in welded joints with ferritic stainless steel ISI 409 and AISI 439 for application in vehicular exhaustion systems", p. 567-574 . In: . São Paulo: Blucher, 2018.
ISSN 2357-7592, DOI 10.5151/simea2018-PAP76

últimos 30 dias | último ano | desde a publicação


downloads


visualizações


indexações